Fe-Cu-Ce,Fe-P-Ce和Fe-Ti-Ce溶液的平衡产物是Ce_2O_2S,而不是Ce与Cu、P、Ti的金属间化合物。测定了Fe液中Ce_2O_2S=2[Ce]+[O]+2[S]反应的平衡常数和溶质之间的相互作用系数。Ce降低Cu和Ti在Fe液中的活度,增大其溶解度,同时增大P的活度,降低其溶解度。
关键词:
铁液
,
Ce
,
Cu
,
P
,
Ti
,
interaction
,
oxygen activity
WANG Yuekui DU Ting Central Iron and Steel Research Institute
,
Ministry of Metallurgical Industry
,
Beijing
,
China
金属学报(英文版)
The equilibrium product in Fe-Cu-Ce,Fe-P-Ce or Fe-Ti-Ce solution have ben Mentified to be Ce_2O_2S,but not the intermetallic compounds of Ce against Cu,P or Ti.The equilibrium eonstant of Ce_2O_2S=2[Ce]+2[O]+[S] and the interaction coefficients between solutes in Fe-base solution have been determined as follows: K_(Ce_2O_2S)=2.57×10~(-5) e_(Ce)~(Cu)=-0.49;e_(Ce)~P=1.77;e_(Ce)~(Ti)=-3.62 e_(Cu)~(Ce)=-0.22;e_P~(Ce)=0.39;e_(Ti)~(Ce)=-1.23 ε_(Ce)~(Cu)=-128.0;ε_(Ce)~P=-224.1;ε_(Ce)~(Ti)=-710.0 Ce decreases the activities of Cu and Ti in Fe-base solution and increases their solubifities,as well as increases the activity of P and decreases its solubility.
关键词:
Fe-base solution
,
null
,
null
,
null
,
null
,
null
,
null
乔海滨
,
刘林
,
赵新宝
,
汤鑫
,
张军
,
傅恒志
,
李相辉
,
曹腊梅
材料工程
doi:10.3969/j.issn.1001-4381.2013.07.015
采用Thermo-calc热力学计算软件以及JMatPro分析软件对DD6镍基单晶高温合金真空感应熔炼过程中氧化物夹杂形成的热力学条件进行了计算分析.结果表明:DD6单晶高温合金熔化和凝固过程中形成的氧化物夹杂主要为Al2O3.热力学平衡状态下,熔化阶段和凝固阶段合金液中氧的活度分别在(3.21～14.0)×10-7,(1.63～4.89)×10-8 范围内.在真空度为0.1Pa时,采用CaO坩埚熔炼DD6合金将会造成熔体增氧和Al2O3夹杂的产生.为了使Al2O3夹杂含量降低至10×10-6以下,合金化开始前应将氧的含量控制在4.709×10-6以内.
关键词:
DD6
,
Al2O3夹杂
,
热力学计算
,
氧活度
夏文勇
,
王一成
,
王明林
,
仇圣桃
钢铁研究学报
促进细小弥散氧化物粒子的析出是提高焊接热影响区韧性的有效手段。通过Al-Ti-O热力学计算,从理论上分析了铝、钛复合脱氧凝固过程中氧化物的析出规律,提出了Ti2O3在凝固前沿形成的热力学条件。试验结果表明,重点对铝、钛加入量和过程氧活度进行控制,可以得到细小的Ti2O3及其复合析出物粒子。对析出物的形貌、尺寸和分布进行了统计分析。